You calculated the percentage by weight correctly.
But your problem is presented ambiguously.
The melting point of an alloy with this composition is over 950°C. The 780°C temperature is only 1 degree above the eutectic temperature, so the time needed to reach equilibrium will be extremely long.
You could find the real composition of the alloy by melting it and slowly cooling it down to 780°C.